- 3003
- UNS A93003
- QQA 250/2
Alloyed with manganese for higher tensile strength than 1100, it has comparable applications as 1100 yet provides slightly higher strength characteristics.
| Chemical Composition Limits (%) |
| SiliconSi |
IronFe |
CopperCu |
ManganeseMn |
MagnesiumMg |
ChromiumCr |
NickelNi |
ZincZn |
TitaniumTi |
OthersEach |
Total |
AluminumMin |
| 0.6 |
0.7 |
0.05-0.2 |
1.0-1.50 |
|
|
|
0.10 |
- |
0.05 |
0.15 |
Remainder |
| Mechanical Property Limits |
View : |
| Alloy and Temper |
Specified Tickness |
Tensil Strength - KSI |
Elongation in 2 inches % |
| Ultimate |
Yield |
| Inches |
Min |
Max |
Min |
Max |
| 3003-0 |
0.006-0.007 |
14.0 |
19.0 |
5.0 |
- |
14 |
| |
0.008-0.012 |
14.0 |
19.0 |
5.0 |
- |
18 |
| |
0.013-0.031 |
14.0 |
19.0 |
5.0 |
- |
20 |
| |
0.032-0.050 |
14.0 |
19.0 |
5.0 |
- |
23 |
| |
0.051-0.249 |
14.0 |
19.0 |
5.0 |
- |
25 |
| |
0.250-3.000 |
14.0 |
19.0 |
5.0 |
- |
23 |
| 3003-H12 |
0.017-0.019 |
17.0 |
23.0 |
12.0 |
- |
3 |
| |
0.020-0.031 |
17.0 |
23.0 |
12.0 |
- |
4 |
| |
0.032-0.050 |
17.0 |
23.0 |
12.0 |
- |
5 |
| |
0.051-0.113 |
17.0 |
23.0 |
12.0 |
- |
6 |
| |
0.114-0.161 |
17.0 |
23.0 |
12.0 |
- |
7 |
| |
0.162-0.249 |
17.0 |
23.0 |
12.0 |
- |
8 |
| |
0.250-0.499 |
17.0 |
23.0 |
12.0 |
- |
9 |
| |
0.500-2.000 |
17.0 |
23.0 |
12.0 |
- |
10 |
| 3003-H14 |
0.009-0.012 |
20.0 |
26.0 |
17.0 |
- |
1 |
| |
0.013-0.019 |
20.0 |
26.0 |
17.0 |
- |
2 |
| |
0.020-0.031 |
20.0 |
26.0 |
17.0 |
- |
3 |
| |
0.032-0.050 |
20.0 |
26.0 |
17.0 |
- |
4 |
| |
0.051-0.113 |
20.0 |
26.0 |
17.0 |
- |
5 |
| |
0.114-0.161 |
20.0 |
26.0 |
17.0 |
- |
6 |
| |
0.162-0.249 |
20.0 |
26.0 |
17.0 |
- |
7 |
| |
0.250-0.499 |
20.0 |
26.0 |
17.0 |
- |
8 |
| |
0.500-1.000 |
20.0 |
26.0 |
17.0 |
- |
10 |
| 3003-H16 |
0.006-0.019 |
24.0 |
30.0 |
21.0 |
- |
1 |
| |
0.020-0.031 |
24.0 |
30.0 |
21.0 |
- |
2 |
| |
0.032-0.050 |
24.0 |
30.0 |
21.0 |
- |
3 |
| |
0.051-0.162 |
24.0 |
30.0 |
21.0 |
- |
4 |
| 3003-H18 |
0.006-0.019 |
27.0 |
- |
24.0 |
- |
1 |
| |
0.020-0.031 |
27.0 |
- |
24.0 |
- |
2 |
| |
0.032-0.050 |
27.0 |
- |
24.0 |
- |
3 |
| |
0.051-0.128 |
27.0 |
- |
24.0 |
- |
4 |
| 3003-H19 |
0.006-0.063 |
29.0 |
- |
- |
- |
1 |
| 3003-H112 |
0.250-0.499 |
17.0 |
- |
10.0 |
- |
8 |
| |
0.500-2.000 |
15.0 |
- |
6.0 |
- |
12 |
| |
2.001-3.000 |
14.5 |
- |
6.0 |
- |
18 |
- Chemical composition is percent maximum unless shown as a range or a minimum.
- Source: Aluminum Standards and Data – The Aluminum Association, Inc.
- Information presented as a guide for reference purposes only and is not intended to be used for product design or application.